Tensile testing is performed as per BISFA rules
|
|
Zero Twist Yarn is tested with a twist of Z-100 TPM
|
|
|
1650 D (1840 Dtex / 1000 Filaments)
|
d.TEX @ 11%M.R.
|
d.Tex
|
1840 ± 55
|
No. of Filaments
|
Nos.
|
1000
|
Yarn
|
Oven Dry Strength
|
Newton
|
100 ± 5
|
Oven Dry Tenacity
|
cN/dTex
|
5.44
|
Oven Dry Elongation @ 44 N
|
%
|
1.8 ± 0.3
|
Oven Dry Elongation @ Break
|
%
|
10.0 ± 1.0
|
Conditioned Strength
|
Newton
|
88 ± 5
|
Conditioned Tenacity
|
cN/dTex
|
4.78
|
Conditioned Elongation @ 44 N
|
%
|
4.5 ± 0.5
|
Conditioned Elongation @ Break
|
%
|
13.5 ± 1.0
|
Finish Type
|
|
SAPCO TF-27 (NOPCO TF-27)
|
Amount of Finish
|
%
|
0.25 ± 0.10
|
Twist 'Z'
|
TPM
|
60 ± 10
|
|
|
1650 D (1840 Dtex / 1000 Filaments)
|
d.TEX @ 11%M.R.
|
d.Tex
|
1840 ± 55
|
No. of Filaments
|
Nos.
|
1000
|
Yarn
|
Twist (manual for testing)
|
TPM
|
100 ± 10
|
Conditioned Strength
|
Newton
|
90 ± 10
|
Conditioned Elongation @ 44 N
|
%
|
6.5 ± 1.5
|
Conditioned Elongation @ Break
|
%
|
14.0 ± 1.5
|
Finish Type
|
|
SAPCO TF-27 (NOPCO TF-27)
|
Amount of Finish
|
%
|
0.25 ± 0.10
|
|
|
2200 D (2440 Dtex / 1350 Filaments)
|
d.TEX @ 11%M.R.
|
d.Tex
|
2440 ± 75
|
No. of Filaments
|
Nos.
|
1350
|
Yarn
|
Twist (manual for testing)
|
TPM
|
100 ± 10
|
Conditioned Strength
|
Newton
|
110 ± 10
|
Conditioned Elongation @ 44 N
|
%
|
3.5 ± 0.5
|
Conditioned Elongation @ Break
|
%
|
14.0 ± 1.5
|
Finish Type
|
|
SAPCO TF-27 (NOPCO TF-27)
|
Yarn Tint
|
-
|
Violet
|
Amount of Finish
|
%
|
0.25 ± 0.10
|
|
|
2200 D (2440 Dtex / 1350 Filaments)
|
d.TEX @ 11%M.R.
|
d.Tex
|
2440 ± 75
|
No. of Filaments
|
Nos.
|
1350
|
Yarn
|
Oven Dry Strength
|
Newton
|
Min. 123
|
Oven Dry Tenacity
|
cN/dTex
|
|
Oven Dry Elongation @ 44 N
|
%
|
1.4 ± 0.3
|
Oven Dry Elongation @ Break
|
%
|
10.5 ± 1.0
|
Conditioned Strength
|
Newton
|
Min. 105
|
Conditioned Tenacity
|
cN/dTex
|
4.51
|
Conditioned Elongation @ 44 N
|
%
|
3.3 ± 0.5
|
Conditioned Elongation @ Break
|
%
|
14.0 ± 1.5
|
Finish Type
|
|
SAPCO TF-27 (NOPCO TF-27)
|
Yarn Tint
|
-
|
Violet
|
Amount of Finish
|
%
|
0.25 ± 0.10
|
Twist 'Z'
|
TPM
|
60 ± 10
|
|